Material: Silicon Carbide (SiC),

To purchase MEMS-related materials, supplies, equipment, wafers, etc.,please visit the links section of the MEMSNet site.

Property↑↓Value↑↓Conditions↑↓Reference↑↓
Tensile strength0.2 GPaCeramic,at temp=20 C,hot pressed.CRC Materials Science and Engineering Handbook, p.405
Tensile strength833.75 .. 3153.75 GPaCeramic,at temp=1400 C,hot pressed.CRC Materials Science and Engineering Handbook, p.405
Tensile strength0.07703 GPaCeramic,at temp=20 C,reaction bondedCRC Materials Science and Engineering Handbook, p.405
Young's Modulus302.8 GPaCeramic,pressureless sintered,at room temperatureCRC Materials Science and Engineering Handbook, p.507
Young's Modulus440 GPaCeramic,hot pressed,at room temperatureCRC Materials Science and Engineering Handbook, p.507
Young's Modulus410.37 GPaCeramic,self bonded, at room temperatureCRC Materials Science and Engineering Handbook, p.507
Young's Modulus430.35 .. 450.37 GPaCeramic,hot pressed, at temp=20 CCRC Materials Science and Engineering Handbook, p.507
Young's Modulus375.03 .. 420.02 GPaCeramic,sintered, at temp=20 CCRC Materials Science and Engineering Handbook, p.507
Young's Modulus350.01 .. 375.02 GPaCeramic,reaction sintered, at temp=20 CCRC Materials Science and Engineering Handbook, p.508
Young's Modulus379.31 GPaCeramic,reaction sintered, at temp=400 CCRC Materials Science and Engineering Handbook, p.508
Young's Modulus365.52 GPaCeramic,reaction sintered, at temp=800 CCRC Materials Science and Engineering Handbook, p.508
Young's Modulus351.72 GPaCeramic,reaction sintered, at temp=1200 CCRC Materials Science and Engineering Handbook, p.508
Young's Modulus200 .. 320 GPaCeramic,reaction sintered, at temp=1400 CCRC Materials Science and Engineering Handbook, p.508
Young's Modulus300 .. 400 GPaCeramic,sintered, at temp=1400 CCRC Materials Science and Engineering Handbook, p.508
Young's Modulus380 GPaCeramic,hot pressed , at temp=1400 CCRC Materials Science and Engineering Handbook, p.508