Material: Silicon Carbide (SiC), bulk

To purchase MEMS-related materials, supplies, equipment, wafers, etc.,please visit the links section of the MEMSNet site.

Property↑↓Value↑↓Conditions↑↓Reference↑↓
Compressive strength0.5655 .. 1.3793 GPaCeramic,at temp=25 CCRC Materials Science and Engineering Handbook, p.419
Density3200 kg/m^3Single crystal.Proceedings of IEEE,Vol 70,No.5,May 1982, p.421
Density3217 kg/m^3hexagonalCRC Materials Science and Engineering Handbook, p.50
Density3210 kg/m^3cubicCRC Materials Science and Engineering Handbook, p.50
Electrical resistivity1 .. 1e+10 Ω*mCeramic,at temp=20 CCRC Materials Science and Engineering Handbook, p.564
Hardness,Knoop(KH)2480 kg/mm/mmSingle crystal.Proceedings of IEEE,Vol 70,No.5,May 1982, p.421
Hardness,Knoop(KH)2960 kg/mm/mm100g,Ceramic,blackCRC Materials Science and Engineering Handbook, p.471
Hardness,Knoop(KH)2745 kg/mm/mm100g,Ceramic,greenCRC Materials Science and Engineering Handbook, p.471
Heat capacity1.09 J/mol/KCeramic,at temp=540 C.CRC Materials Science and Engineering Handbook, p.262
Heat capacity1.13 J/mol/KCeramic,at temp=700 C.CRC Materials Science and Engineering Handbook, p.262
Heat capacity1.25 J/mol/KCeramic,at temp=1000 C.CRC Materials Science and Engineering Handbook, p.262
Heat capacity1.34 J/mol/KCeramic,at temp=1200 C.CRC Materials Science and Engineering Handbook, p.262
Heat capacity1.38 J/mol/KCeramic,at temp=1350 C.CRC Materials Science and Engineering Handbook, p.262
Heat capacity1.46 J/mol/KCeramic,at temp=1550 C.CRC Materials Science and Engineering Handbook, p.262
Modulus of Rupture0.1862 GPaCeramifc,at room temperatureCRC Materials Science and Engineering Handbook, p.532
Modulus of Rupture0.1724 GPaCeramic,at temp=1300 CCRC Materials Science and Engineering Handbook, p.532
Modulus of Rupture0.07586 GPaCeramic,at temp=1400 CCRC Materials Science and Engineering Handbook, p.532
Modulus of Rupture0.1034 GPaCeramic,at temp=1800 CCRC Materials Science and Engineering Handbook, p.532
Modulus of Rupture0.2897 GPaCeramic,with 1 wt% B addictiveCRC Materials Science and Engineering Handbook, p.532
Poisson's Ratio0.183 .. 0.192Ceramic,at room temperature,density=3128 kg/m/m/mCRC Materials Science and Engineering Handbook, p.537
Tensile strength0.03448 .. 0.1379 GPaCeramic,at temp=25 CCRC Materials Science and Engineering Handbook, p.405
Thermal conductivity350 W/m/KSingle crystal.Proceedings of IEEE,Vol 70,No.5,May 1982, p.421
Yield strength21 GPaSingle crystal.Proceedings of IEEE,Vol 70,No.5,May 1982, p.421
Young's Modulus700 GPaSingle crystal.Proceedings of IEEE,Vol 70,No.5,May 1982, p.421
Young's Modulus401.38 GPaCeramic,density=3128 kg/m/m/m, at room temperatureCRC Materials Science and Engineering Handbook, p.507
Young's Modulus410.47 GPaCeramic,density=3120 kg/m/m/m, at room temperatureCRC Materials Science and Engineering Handbook, p.507