Material: Glass (SiO2), bulk
To purchase MEMS-related materials, supplies, equipment, wafers, etc.,please visit the links section of the MEMSNet site.
| Property↑↓ | Value↑↓ | Conditions↑↓ | Reference↑↓ |
|---|---|---|---|
| Coefficient of static friction | 0.15 | Used as a mover,min voltage to remove the mover=1128 V, bottom of the mover is glass plate | IEEE Micro Electro Mechanical Systems Workshop,Jan-Feb 1991, Nara,Japan, p.151 |
| Coefficient of static friction | 0.14 | Used as a mover,min voltage to move the mover=950 V, bottom of the mover is Silicon substrate,thickness=1.1 mm. | IEEE Micro Electro Mechanical Systems Workshop,Jan-Feb 1991, Nara,Japan, p.151 |
| Electrical resistivity | 1e+09 .. 3.98e+11 Ω*m | Glass,at temp=250 C | CRC Materials Science and Engineering Handbook, p.568 |
| Electrical resistivity | 3.16e+06 .. 6.3e+08 Ω*m | Glass,at temp=400 C | CRC Materials Science and Engineering Handbook, p.568 |
| Electrical resistivity | 630000 Ω*m | Glass,at temp=500 C | CRC Materials Science and Engineering Handbook, p.568 |
| Electrical resistivity | 4600 Ω*m | Glass,at temp=1000 C | CRC Materials Science and Engineering Handbook, p.568 |
| Electrical resistivity | 790 Ω*m | Glass,at temp=1500 C | CRC Materials Science and Engineering Handbook, p.568 |
| Hardness,Knoop(KH) | 500 .. 679 kg/mm/mm | Glass | CRC Materials Science and Engineering Handbook, p.476 |
| Poisson's Ratio | 0.166 .. 0.177 | Glass,at room temperature | CRC Materials Science and Engineering Handbook, p.540 |
| Shear Modulus | 0.001624 GPa | Glass,at 1096 C(straining point) | CRC Materials Science and Engineering Handbook, p.529 |
| Shear Modulus | 0.001597 GPa | Glass,at 998 C(annealing point) | CRC Materials Science and Engineering Handbook, p.529 |
| Shear Modulus | 0.001493 GPa | Glass,at temp=20 C | CRC Materials Science and Engineering Handbook, p.529 |
| Static frictional force(max) | 0.000517 N | Used as a mover,min voltage to remove the mover=1128 V, bottom of the mover is glass plate | IEEE Micro Electro Mechanical Systems Workshop,Jan-Feb 1991, Nara,Japan, p.151 |
| Static frictional force(max) | 0.000367 N | Used as a mover,min voltage to move the mover=950 V, bottom of the mover is Silicon substrate,thickness=1.1 mm. | IEEE Micro Electro Mechanical Systems Workshop,Jan-Feb 1991, Nara,Japan, p.151 |
| Tensile strength | 49.6 kg/mm/mm | Glass,48 um diameter fiber | CRC Materials Science and Engineering Handbook, p.409 |
| Tensile strength | 44.3 kg/mm/mm | Glass,56 um diameter fiber | CRC Materials Science and Engineering Handbook, p.409 |
| Tensile strength | 42.3 kg/mm/mm | Glass,60 um diameter fiber | CRC Materials Science and Engineering Handbook, p.409 |
| Tensile strength | 39.7 kg/mm/mm | Glass,65 um diameter fiber | CRC Materials Science and Engineering Handbook, p.409 |
| Tensile strength | 36.5 kg/mm/mm | Glass,74 um diameter fiber | CRC Materials Science and Engineering Handbook, p.409 |
| Tensile strength | 35.8 kg/mm/mm | Glass,78 um diameter fiber | CRC Materials Science and Engineering Handbook, p.409 |
| Tensile strength | 28.8 kg/mm/mm | Glass,108 um diameter fiber | CRC Materials Science and Engineering Handbook, p.409 |
| Tensile strength | 28.3 kg/mm/mm | Glass,112 um diameter fiber | CRC Materials Science and Engineering Handbook, p.409 |
| Tensile strength | 5.6 kg/mm/mm | Glass,corning 7940 silica glass at 100 C | CRC Materials Science and Engineering Handbook, p.409 |
| Tensile strength | 5.6 kg/mm/mm | Glass,corning 7940 silica glass at 100 C | CRC Materials Science and Engineering Handbook, p.409 |
| Tensile strength | 6.2 kg/mm/mm | Glass,corning 7940 silica glass at 300 C | CRC Materials Science and Engineering Handbook, p.409 |
| Tensile strength | 6.6 kg/mm/mm | Glass,corning 7940 silica glass at 500 C | CRC Materials Science and Engineering Handbook, p.409 |
| Tensile strength | 7.1 kg/mm/mm | Glass,corning 7940 silica glass at 700 C | CRC Materials Science and Engineering Handbook, p.409 |
| Tensile strength | 7.6 kg/mm/mm | Corning 7940 silica glass at 900 C | CRC Materials Science and Engineering Handbook, p.409 |